Being the market leader in the domain, we are actively devoted towards providing best quality Latex Gloves at an amazing price to our clients. These are a type of disposable medical glove, made 100% out of latex. Our provided gloves are a popularchoice in industrial, domestic and medical tasks. Offered gloves are available in different in sizes to meet customer needs. These Latex Gloves are available in un-powdered or powdered materials. They are highly durable and act as a great barrier against chemical solutions.

Features:

  • Excellent fit for comfort, sensitivity and safety
  • High anti tear properties
  • Textured to improve grip

Quality Standards

  • Conforms to ASTM D3578 and EN455 Standards
  • Manufactured under QSR (GMP), ISO9001:2008 Quality Management System
  • Using FDA approved absorbale corn starch, USP grade.

Glove Sizes

  • Extra-small, Small, Medium, Large, Extra-large
  • Marked in the check box on the shipping carton with black ink

Product Specifications

Type

Powdered & Powder-free, non sterile

Material

Natural high quality latex

Design & Features

Powdered: Ambidextrous,smooth or textured surface, beaded cuff, natural white, coloured or mint flavoured, USP grade absorbable corn starch Powder-Free (Polymer Coated or online chlorinated).

Ambidextrous: Smooth or textured surface, beaded cuff, off-white to yellow, coloured or mint flavoured.

Storage

The gloves shall maintain their properties when stored in a dry condition at temperature not higher than 30°C.

Shelf-life

5 years from date of manufacturing

Physical Dimensions

Dimensions

Standards

Top Glove

ASTM D3578

Length (mm)

Min 240

Min 220 ( XS, S)
Min 230 (M, L, XL)

Width (mm)



Extra-Small

76+3

70+10

Small

84+3

80+10

Medium

94+3

95+10

Large

105+3

111+10

Extra-large

113+3


Thickness-Single wall (mm)



Fingers

Palm

Min 0.08
Min 0.08
Min 0.08
Min 0.08

Physical properties


Property

ASTM D3578

Elongation at break (%)


Before Aging

Min 650

After Aging

Min 500

Tensile strength (Mpa)


Before Aging

Min 18

After Aging

Min 14